Flux-Cored Arc Welding (FCAW) utilizes a continuously-fed tubular electrode, electrical power to melt the electrode, and may or may not use shielding gas from an externally supplied source when depositing material in the weld joint. The flux-cored electrode is a composite tubular filler metal consisting of a metal sheath with a core of mineral compounds and powdered metals. The resulting weld bead is covered by a residual slag (melted and solidified flux) which helps to protect and shape the finished weld, and is generally easily removed upon completion of the weld. Flux Cored Welding combines the high productivity of MIG welding using a solid electrode with the ability to weld on more contaminated base material. When compared with MIG welding, higher deposition rates are possible, especially when welding out of position.
There are three types of flux-cored wires available:
Each has its own advantages.
The type of Flux Cored Welding wire used depends on the welding position, the mechanical properties required, the type of joint and its fit-up, and the environment in which the welding is to be performed. Generally, self-shielded wires are used for welding outside or for special applications such as welding galvanized steel. Among the most common are outdoor construction and fabrication in areas where gas cylinders and gas shielding cannot be readily used. Gas-shielded flux-cored wires are used in operations such as shop fabrication, maintenance, and shipbuilding. Flux-cored wire welding is especially useful where the base material to be welded has some amount of scale, rust or other surface contaminants present. With the proper selection of wire type and shielding gas, weld properties are excellent for many types of materials.
All-position wires (E-71T-1) are typically smaller than 1/16” in diameter and are formulated with a fast-freeze flux. They are not well suited for use where high levels of base metal contamination exist, but offer good control when welding in the vertical up or over-head position. Shielding gas selection can be pure CO2 or C25. In all instances, the shielding gas selected should be matched with the recommendation of the filler metal manufacturer. Failure to do so may result in poor quality welds. A common problem from incorrect gas selection is weld cracking.
Flat-position wires (E-70) can be utilized in the flat or horizontal welding positions. They are typically greater than 1/16” diameter and are primarily applied for high deposition welding on thicker base materials (>1/4”) This family of wires offers a greater resistance to base metal contamination, and they have been shown to perform well over some rust and mill scale. Good welding practice dictates that the base metal should be cleaned of contamination prior to welding but, if this is not possible, these wires are the preferred choice.
Why use Flux Cored Welding?
What are some limitations of Flux Cored Welding?